When the content of silicon up to 4% silicon bronze has good casting properties and ductility. Usually it is with the addition of manganese or nickel, and sometimes aluminum, zinc, tin or iron. With its high resilient and mechanical properties, and as a corrosion-resistant and wear-resistant, is of great interest to the industry.
Bronzes of this type are soldered perfectly hot and cold solder perfectly handled the pressure and welded with steel, bronze and others. Silicon bronze surpass tin on corrosion resistance and mechanical properties, are non-magnetic and hardy, do not give a spark when striking.When the content of silicon up to 4% silicon bronze has good casting properties and ductility. Usually it is with the addition of manganese or nickel, and sometimes aluminum, zinc, tin or iron. With its high resilient and mechanical properties, and as a corrosion-resistant and wear-resistant, is of great interest to the industry.
Bronzes of this type are soldered perfectly hot and cold solder perfectly handled the pressure and welded with steel, bronze and others. Silicon bronze surpass tin on corrosion resistance and mechanical properties, are non-magnetic and hardy, do not give a spark when striking. High-strengthto dry gases and alkaline media, so are used to produce gas, chemical waste pipes. This bronze is also used for the production of spring parts operating at elevated temperatures (not deformed). Semi-finished products in the form of wire, strip, bars, sheets used in general mechanical engineering and marine shipbuilding, for the manufacture of pipes, screens, meshes, smoke filters, evaporators, in engine construction. They stand in the sea and fresh water.
Nickel in silicon Bonzo after quenching and tempering of the alloy increases the hardness of up to 300%. The same actions have chrome and cobalt. These bronzes are used in the manufacture of parts critical applications. When the tin content of up to 0.5% rise corrosive properties. The presence of 1% zinc in the alloy facilitates the melting process. The high aluminum content in the alloy increases its hardness and strength, but the quality of the hydraulic lost. lead and zinc are added to improve the fluidity and decrease the porosity usadistoy alloy, which in turn reduces the cost, but the disadvantage of the alloy is more prone to absorb gases.
to dry gases and alkaline media, so are used to produce gas, chemical waste pipes. This bronze is also used for the production of spring parts operating at elevated temperatures (not deformed). Semi-finished products in the form of wire, strip, bars, sheets used in general mechanical engineering and marine shipbuilding, for the manufacture of pipes, screens, meshes, smoke filters, evaporators, in engine construction. They stand in the sea and fresh water.
Nickel in silicon Bonzo after quenching and tempering of the alloy increases the hardness of up to 300%. The same actions have chrome and cobalt. These bronzes are used in the manufacture of parts critical applications. When the tin content of up to 0.5% rise corrosive properties. The presence of 1% zinc in the alloy facilitates the melting process. The high aluminum content in the alloy increases its hardness and strength, but the quality of the hydraulic lost. lead and zinc are added to improve the fluidity and decrease the porosity usadistoy alloy, which in turn reduces the cost, but the disadvantage of the alloy is more prone to absorb gases.

Download Non-Ferrous Metals Catalogue in PDF